09CrCuSb (enterprise code ND steel) is a steel resistant to sulfuric acid low temperature dew point corrosion (ND steel plate, ND steel pipe, 09CrCuSb steel plate, 09CrCuSb steel pipe, etc.). Usually called 09 chromium copper antimony.
09CrCuSb (ND steel) is a hot-rolled steel plate and steel pipe with excellent resistance to sulfuric acid dew point corrosion developed for the purpose of heat exchange, smoke pipes, chimneys, boiler air preheaters, economizers, heat exchangers, condenser coolers, evaporators, etc. for coal-fired boilers, oil-fired boilers, electric furnaces. Its superior resistance to sulfuric acid dew point corrosion and very high cost performance make it the best material that can completely replace stainless steel and surpass stainless steel (in terms of resistance to sulfuric acid dew point corrosion). ND steel has great economic significance and conforms to today’s “green” concepts such as high efficiency, longevity, energy saving, and environmental protection, as well as the national development policy orientation.
ND steel, namely 09CrCuSb steel, is the most ideal steel material for “resistance to low-temperature dew point corrosion of sulfuric acid” at home and abroad. ND steel is widely used in the manufacture of economizers, air preheaters, heat exchangers and evaporators that serve in high-sulfur flue gas to resist dew point corrosion of sulfur-containing flue gas. ND steel also has the ability to resist chloride ion corrosion. The main reference index of ND steel pipe (immersion in 50% H2SO4 solution at 70 degrees Celsius for 24 hours) is higher than that of carbon steel, similar steel imported from Japan, and stainless steel in terms of corrosion resistance. The product has been widely praised by major domestic refineries and manufacturing units after use. The carbon content in the steel is low and has achieved good results.
09CrCuSb(即ND钢)
机械性能 MECHANICAL PROPERITIES
| 牌号 GRADE | 抗拉强度(Mpa)
T.S |
屈服强度(Mpa)
Y.S |
伸长率(%)
E.L |
| 09CrCuSb | 390-550 | ≥245 | ≥25 |
化学成份 CHEMICAL PROPERITIES
| 牌号 | 化学成分(%) | |||||||
| GRADE | C | Si | Mn | Cr | Cu | Sb | P | S |
| 09CrCusb | ≤0.10 | 0.20-0.40 | 0.35-0.65 | 0.70-1.20 | 0.25-0.45 | ≤0.10 | ≤0.10 | ≤0.10 |
GB 150.2-2011中的化学成分
| 牌号 | 化学成分(%) | |||||||
| GRADE | C | Si | Mn | P | S | Cr | Cu | Sb |
| 09CrCuSb | ≤0.12 | 0.20~0.40 | 0.35~0.65 | ≤0.030 | ≤0.020 | 0.70~1.10 | 0.25~0.45 | 0.04~0.10 |
09CrCuSb钢(ND钢)同其它钢种的比较 COMPARIRATION
| 钢种 | 09CrCuSb(ND钢) | CRIR(日本) | 1Cr18Ni9 | Corten | S-TEN(日本) | A3(Q235B) |
| 腐蚀速度 | 7.30 | 13.40 | 21.70 | 63.00 | 27.4 | 103.50 |
| 倍数 | 1 | 1.84 | 2.97 | 8.63 | 3.75 | 14.11 |